Caracterização de amostra de espuma de alumínio Liga 6101-T6 por meio de análise de porosidade, corrosão e resistividade
| dc.contributor.advisor | Gianelli, Bruno Fernando | |
| dc.contributor.author | Raphael, Igor | |
| dc.contributor.referee | Goulart, Pedro Roberto | |
| dc.contributor.referee | Nossa, Tamires de Souza | |
| dc.date.accessioned | 2024-03-01T14:15:31Z | |
| dc.date.available | 2024-03-01T14:15:31Z | |
| dc.date.issued | 2023-12-01 | |
| dc.description.abstract | O alumínio, é um material metálico amplamente disponível na crosta terrestre na forma de óxido e, após processamento, possui diversas propriedades vantajosas, tais como baixa densidade (cerca de um terço da densidade do ferro) e boa resistência mecânica proporcionalmente à sua densidade. É amplamente empregado nos mais diversos setores da indústria, estima-se que 80% do peso de um avião moderno é composto por alumínio. A partir da década de 40, foi desenvolvida uma nova técnica para fabricação do alumínio na forma de espuma metálica, possibilitando uma gama totalmente nova de aplicações na indústria. Assim como diversos materiais, esse metal também é suscetível à corrosão, logo diversos métodos de proteção superficial foram desenvolvidos, dentre esses, o processo de anodização. Este trabalho tem como objetivo compreender e comparar o efeito da anodização em amostras de espuma de alumínio liga 6101T. Para tal, foi feita a caracterização de duas amostras da liga, na forma de espuma metálica, sendo uma amostra estudada sem anodização e outra após este tratamento superficial. A comparação dos efeitos da anodização foi realizada por meio das análises das porosidades das amostras, do comportamento sob corrosão e das resistividades. Mostrando que o tratamento superficial resultou em um aumento da área dos poros, melhora na resistência à corrosão e não alterou a resistividade das amostras. | |
| dc.description.abstract2 | Aluminum is a metallic material that is widely available in the earth's crust in oxide form and, after processing, has several advantageous properties, such as low density (about a third of the density of iron) and good mechanical strength in proportion to its density. It is widely used in the most diverse sectors of industry, and it is estimated that 80% of the weight of a modern aircraft is made up of aluminum. In the 1940s, a new technique was developed for manufacturing aluminum in the form of metallic foam, enabling a whole new range of applications in industry. Like many materials, this metal is also susceptible to corrosion, so various methods of surface protection have been developed, including the anodizing process. The aim of this work is to understand and compare the effect of anodizing on aluminium alloy 6101T foam samples. To this end, two samples of the alloy were characterized in the form of metallic foam, one of which was studied without anodizing and the other after this surface treatment. The effects of anodizing were compared by analyzing sample porosity, corrosion behaviour and resistivity. This showed that the surface treatment resulted in an increase in pore area, improved corrosion resistance and did not alter the resistivity of the samples. | |
| dc.format.mimetype | application/pdf | |
| dc.identifier.bibliographicCitation | RAPHAEL, Igor. Caracterização de amostra de espuma de alumínio Liga 6101-T6 por meio de análise de porosidade, corrosão e resistividade. Itapetininga, 2023. 83 f. Trabalho de Conclusão de Curso (Bacharelado em Engenharia Mecânica) - Instituto Federal de Educação, Ciência e Tecnologia de São Paulo, Campus Itapetininga, Itapetininga, 2023. | |
| dc.identifier.uri | 123456789/624 | |
| dc.publisher | Instituto Federal de Educação, Ciência e Tecnologia de São Paulo (IFSP) | |
| dc.publisher.campi | ITAPETININGA | |
| dc.subject.keywords | Ligas de alumínio | |
| dc.subject.keywords | Porosidade | |
| dc.subject.keywords | Alumínio - corrosão | |
| dc.title | Caracterização de amostra de espuma de alumínio Liga 6101-T6 por meio de análise de porosidade, corrosão e resistividade | |