Otimização de parâmetros para soldagem GTAW do aço inoxidável duplex UNS S32205

dc.contributor.advisorCruz Junior, Eli Jorge da
dc.contributor.authorBertoco Junior, Marcelo
dc.contributor.refereeVarasquim, Francisco Mateus Faria de Almeida
dc.contributor.refereeLemos, Gabriela Pereira
dc.date.accessioned2024-03-13T13:34:14Z
dc.date.available2024-03-13T13:34:14Z
dc.date.issued2022-11-30
dc.description.abstractOs aços inoxidáveis duplex tem sido cada vez mais utilizados na indústria, devido as suas características que combinam boas propriedades mecânicas e de resistência à corrosão. Esses aços apresentam uma estrutura bifásica, sendo 50% de ferrita e 50% de austenita. Desse modo, desenvolver técnicas e conhecer os melhores parâmetros para o processo de soldagem desses materiais é fundamental, para que o balanço de fases e as propriedades do material não sejam severamente prejudicados durante o processo. Este trabalho tem o objetivo de estudar o comportamento dos aços inoxidáveis duplex UNS S32205 quando soldados pelo processo GTAW (Gas Tungsten Arc Welding) no que diz respeito a influência do processo nas microestruturas destes aços, com foco na otimização de parâmetros para avaliação do aporte térmico empregado, levando em consideração as variáveis de corrente, tensão, eficiência e velocidade de soldagem. Foram realizadas soldagens na condição autógena com aporte térmico variando entre 147,9J/mm e 369,75J/mm. Seguiu-se com a análise do metal base e dos cordões de solda mediante microscopia óptica (MO). Os resultados apresentaram a região do metal de solda com fração volumétrica de austenita variando entre 17% e 26,6%. Esse resultados e deve as variações das taxas de resfriamento, pois quando esta diminui, há maior formação de austenita. Na zona termicamente afetada (ZTA) mais próxima ao metal de solda, percebe-se a formação de uma faixa com maior percentual de ferrita. Isso acontece devido às temperaturas de pico atingida, durante a soldagem, em que a austenita se torna instável. Dessa maneira, a ferrita não se transforma em austenita, pois há um rápido resfriamento no processo de soldagem.
dc.description.abstract2Duplex stainless steels have been increasingly used in industry, due to their characteristics that combine good mechanical properties and corrosion resistance. These steels have a biphasic structure, being 50% ferrite and 50% austenite. Thus, developing techniques and knowing the best parameters for the welding process of these materials is fundamental, so that the phase balance and material properties are not severely impaired during the process. This work aims to study the behavior of UNS S32205 duplex stainless steels when welded by the GTAW (Gas Tungsten Arc Welding) process, with regard to the influence of the process on the microstructures of these steels, focusing on the optimization of parameters for evaluating the heat input employed, taking into account the variables of current, voltage, efficiency and welding speed. Weldings were carried out in the autogenous condition with heat input varying between 147.9 J/mm and 369.75 J/mm. This was followed by the analysis of the base metal and weld beads using optical microscopy (OM). The results showed the region of the weld metal with austenite volume fraction varying between 17% and 26.6%. This result is due to variations in cooling rates, because when it decreases, there is greater formation of austenite. In the heat-affected zone (TAZ) closest to the weld metal, the formation of a band with a higher percentage of ferrite can be seen. This happens due to the peak temperatures reached during welding, in which the austenite becomes unstable. Due to lack of time, ferrite does not transform into austenite, as there is rapid cooling in the welding process.
dc.format.mimetypeapplication/pdf
dc.identifier.bibliographicCitationBERTOCO JUNIOR, M. Otimização de parâmetros para soldagem GTAW do aço inoxidável duplex UNS S3220. Itapetininga, 2022. 43 f. Trabalho de Conclusão de Curso (Bacharelado em Engenharia Mecânica) - Instituto Federal de Educação, Ciência e Tecnologia de São Paulo, Câmpus Itapetininga, Itapetininga, 2022.
dc.identifier.urihttps://repositorio.ifsp.edu.br/handle/123456789/691
dc.identifier2.latteshttp://lattes.cnpq.br/7575090078005630
dc.publisherInstituto Federal de Educação, Ciência e Tecnologia de São Paulo (IFSP)
dc.publisher.campiITAPETININGA
dc.subject.keywordsSoldagem
dc.subject.keywordsAço inoxidável
dc.subject.keywordsSoldagem e corte oxiacetilênico
dc.titleOtimização de parâmetros para soldagem GTAW do aço inoxidável duplex UNS S32205
dc.typeTrabalhos de Conclusão de Curso de Graduação
Arquivos
Pacote Original
Agora exibindo 1 - 1 de 1
Carregando...
Imagem de Miniatura
Nome:
bertocojunior_m_tcc_itp.pdf
Tamanho:
17.06 MB
Formato:
Adobe Portable Document Format
Descrição:
Licença do Pacote
Agora exibindo 1 - 1 de 1
Carregando...
Imagem de Miniatura
Nome:
license.txt
Tamanho:
1.92 KB
Formato:
Item-specific license agreed upon to submission
Descrição: