Otimização dos parâmetros de soldagem no processo GTAW de AISD UNS S32750
| dc.contributor.advisor | Cruz Junior, Eli Jorge da | |
| dc.contributor.author | Tominaga, Daniel Kazuyoshi | |
| dc.contributor.referee | Varasquim, Francisco Mateus Faria de Almeida | |
| dc.contributor.referee | Lemos, Gabriela Pereira | |
| dc.date.accessioned | 2024-03-05T16:01:57Z | |
| dc.date.available | 2024-03-05T16:01:57Z | |
| dc.date.issued | 2022-11-30 | |
| dc.description.abstract | Os aços inoxidáveis super duplex (AISD) são caracterizados por uma microestrutura bifásica composta por proporções semelhantes de austenita e ferrita, que promovem excelente resistência mecânica e resistência à corrosão. Após submeter o AISD ao processo de soldagem, normalmente apresenta microestrutura desbalanceada, predominante ferrítica, que compromete suas propriedades mecânicas e estruturais. Para tanto, a otimização dos métodos de soldagem se fazem necessários de modo a garantir o balanço de fases e propriedades do material não sejam afetadas no processo. No presente trabalho foi analisado a caracterização das juntas soldadas com o processo GTAW (Gas Tungsten Arc Welding) em chapas de aço inoxidável super duplex UNS S32750 com 1,5 mm de espessura, com objetivo em investigar o efeito do aporte térmico na microestrutura do metal de solda. Foram realizadas soldagens na condição autógena com variação do aporte térmico entre147,9J/mm e 369,8J/mm. Como gás de proteção utilizou-se argônio puro com vazão de 10 l/min. A caracterização microestrutural foi realizada através de microscopia ótica. Os resultados apresentaram a região do metal de solda com fração volumétrica deaustenita variando entre de 19,62% e 30,4%.Em relação à microestrutura da zona termicamente afetada (ZTA) do metal de solda, observou-se uma ferritização da mesma com pequena fração volumétrica de austenita nas regiões de contorno de grão. Não se identificou a presença de fases frágeis no material. | |
| dc.description.abstract2 | Super duplex stainless steels (SDSS) are characterized by a two-phase microstructure composed of similar combinations of austenite and ferrite, which promote excellent mechanical strength and resistance to weathering. After being submitted to the SDSS to the suffering process, it normally presents an unbalanced microstructure, predominantly ferritic, which compromises its mechanical and emotional properties. Therefore, the optimization of the experimental methods is necessary in order to guarantee the balance of phases and material properties are not supported in the process. In the present work, the characterization ofjoints welded with the GTAW (Gas Tungsten Arc Welding) process in super duplex stainless steel plates UNS S32750 with 1.5 mm thickness was analyzed, with the aim of investigating the effect of heat input on the microstructure of the metal. soldering. Weldings were carried out in the automatic condition with variation of the thermal input between 147.9J/mm and 369.8J/mm. As a shielding gas, pure argon was used with a flow rate of 10 l/min. The microstructural characterization was performed using optical microscopy. The results showed the weld metal region with austenite volumetric revenue varying between 19.62% and 30.4%. Regarding the microstructure of the thermally stabilized zone (TAZ) of the weld metal, a ferritization of the same was observed with smallvolumetric uptake of austenite in the grain boundary regions. The presence of unstable phases in the material was not identified. | |
| dc.format.mimetype | application/pdf | |
| dc.identifier.bibliographicCitation | TOMINAGA, D. K. Otimização dos parâmetros de soldagem no processo GTAW de AISD UNS S32750. Itapetininga, 2022. 30 f. Trabalho de Conclusão de Curso (Bacharelado em Engenharia Mecânica) - Instituto Federal de Educação, Ciência e Tecnologia de São Paulo, Câmpus Itapetininga, Itapetininga, 2022. | |
| dc.identifier.uri | https://repositorio.ifsp.edu.br/handle/123456789/634 | |
| dc.publisher | Instituto Federal de Educação, Ciência e Tecnologia de São Paulo (IFSP) | |
| dc.publisher.campi | ITAPETININGA | |
| dc.subject.keywords | Soldagem | |
| dc.subject.keywords | Aço inoxidável | |
| dc.subject.keywords | Metalografia | |
| dc.title | Otimização dos parâmetros de soldagem no processo GTAW de AISD UNS S32750 | |
| dc.type | Trabalhos de Conclusão de Curso de Graduação |