Soldagem do aço inoxidável austenítico AISI 316L pelo processo Friction Stir Welding
| dc.contributor.advisor | Cruz Junior, Eli Jorge da | |
| dc.contributor.author | Bueno, Marcelo Henrique Monen | |
| dc.contributor.referee | Varasquim, Francisco Mateus Faria de Almeida | |
| dc.contributor.referee | Lemos, Gabriela Pereira | |
| dc.date.accessioned | 2024-03-01T18:18:00Z | |
| dc.date.available | 2024-03-01T18:18:00Z | |
| dc.date.issued | 2023-12-07 | |
| dc.description.abstract | Utilizando do processo de solda por atrito foi estudado o resultado do cordão de solda obtido em chapas do aço inox AISI 316L. Para a realização do processo foi utilizado uma ferramenta de aço duro (carboneto de tungstênio) com pino cônico acoplada ao centro de usinagem de cinco eixos da marca Pinnacle AX450,as variáveis de avanço de penetração e de avanço linear foram fixadas em 5 mm/min e 30 mm/min respectivamente, já as velocidades de rotação utilizadas variaram de 800 rpma2000 rpm.Com os resultados obtidos foi possível entender o comportamento da microestrutura do metal ao longo do cordão de solda que apresentou um refinamento de grão bom no sentido do deslocamento da ferramenta, essa análise foi realizada através do estudo da metalografia dos corpos de prova. Além disso, verificou-seo desgaste acentuado das ferramentas utilizadas que evidenciaram que os parâmetros considerados não são ideais para a realização desse tipo de junção com as variáveis mencionadas, essa falha da ferramenta também mostrou que o formato do pino escolhido não influenciou positivamente do processo e que isso também foi um fator que influenciou nas falhas. | |
| dc.description.abstract2 | Using the friction welding process, the result of the weld bead obtained on AISI 316L stainless steel sheets was studied. To carry out the process, a hard steel tool (tungsten carbide) with a conical pin was used coupled to the Pinnacle AX450 five-axis machining center, the penetration feed and linear feed variables were set at 5 mm/min. and 30 mm/min respectively, the rotation speeds used varied from 800 rpm to 2000 rpm. With the results obtained, it was possible to understand the behavior of the metal microstructure along the weld bead, which showed good grain refinement in the direction of tool displacement. This analysis was carried out through the study of the metallography of the specimens. Furthermore, there was significant wear on the tools used, which showed that the parameters considered are not ideal for carrying out this type of joint with the variables mentioned. This tool failure also showed that the shape of the pin chosen did not positively influence the process. and that this was also a factor that influenced the failures. | |
| dc.format.mimetype | application/pdf | |
| dc.identifier.bibliographicCitation | BUENO, M. H. M. Soldagem do aço inoxidável austenítico AISI 316L pelo processo Friction Stir Welding. Itapetininga, 2023. 43 f. Trabalho de Conclusão de Curso (Bacharelado em Engenharia Mecânica) - Instituto Federal de Educação, Ciência e Tecnologia de São Paulo, Campus Itapetininga, Itapetininga, 2023. | |
| dc.identifier.uri | https://repositorio.ifsp.edu.br/handle/123456789/627 | |
| dc.publisher | IFSP | |
| dc.publisher.campi | ITAPETININGA | |
| dc.subject.keywords | Solda e soldagem | |
| dc.subject.keywords | Atrito | |
| dc.subject.keywords | Aço inoxidável | |
| dc.title | Soldagem do aço inoxidável austenítico AISI 316L pelo processo Friction Stir Welding | |
| dc.type | Trabalhos de Conclusão de Curso de Graduação |